耐諾氧化鋯球(NanorZr-95B):
      采用氧化釔作穩(wěn)定，干粉等靜壓成型，燒結定相的工藝制成。PPM級的磨耗和優(yōu)異的抗剪切性特別適合籃式砂磨機、立式攪拌磨、臥式滾動磨、振動磨等設備對拒絕污染的漿料和粉料的濕法和干法的超細分散和研磨。
氧化鋯含量: 95%,                 氧化釔含量: 5%,
比      重: >6.0kg/dm³,        散      重: >3.6kg/L,
莫 氏 硬度: 9,                       維 氏 硬度: >1200kg/mm²,
斷 裂 韌性: 10Mpa.m^1/2     彈 性 模量: 200Gpa, 
粒      徑: 3-50mm,              顏      色: 奶白,
包      裝: 25kg/桶.
NanorZr-95B zirconiium oxide balls are manufactured from dry Yttria Stabilized Zirconi powder by high compaction press. Then was sintered at a high temperature to form a Tetragonal Zirconia Polycrystal(Y-TZP) microstructure. The highest crushing strength and fracture toughness was considered the first choice of grinding media to mill the contamination-free powder or slurry. 
ZrO₂ %: 95 ,                            Y₂O₃ %: 5
Density: >6.0kg/dm³,            Hardness Vickers: >1200kg/mm²
Toughness: 10Mpa.m1/2,      Crushing Strength: 2300N (2mm)
Sizes: 3-50mm ,                     Packing: 25kg/bucket